Indexado em
- Abra o Portão J
- Genamics JournalSeek
- Diretório de Periódicos de Ulrich
- RefSeek
- Diretório de Indexação de Periódicos de Pesquisa (DRJI)
- Universidade de Hamdard
- EBSCO AZ
- OCLC- WorldCat
- Invocação Proquest
- Scholarsteer
- publons
- Fundação de Genebra para Educação e Pesquisa Médica
- Euro Pub
- Google Scholar
Links Úteis
Compartilhe esta página
Folheto de jornal
Periódicos de Acesso Aberto
- Agro e Aquicultura
- Alimentos e Nutrição
- Bioinformática e Biologia de Sistemas
- Bioquímica
- Ciência de materiais
- Ciencias ambientais
- Ciências Clínicas
- Ciências Farmacêuticas
- Ciências gerais
- Ciências Médicas
- Cuidados de enfermagem e saúde
- Engenharia
- Genética e Biologia Molecular
- Gestão de negócios
- Imunologia e Microbiologia
- Neurociência e Psicologia
- Química
Abstrato
Facilitated Transport of CO2 through EA-Mediated Poly(Vinyl alcohol)Membrane Cross-Linked by Formaldehyde
Mohammadreza Omidkhah, Mona Zamani Pedram and Abtin Ebadi Amooghin
In this work, the cross-linked poly (vinyl alcohol)/formaldehyde with different blend compositions (FA/PVA: 1, 3, 5 ratio%) were synthesized. In addition, different diethanolamine concentrations ranging from 15-45 wt % were investigated for membrane fabrication. Moreover, the membranes were characterized by Fourier transform infrared (FTIR) and scanning electron microscopy (SEM) and contact angle measurement. Furthermore, the effects of crosslinking agent content, amine concentration and feed pressure on CO2/CH4 transport properties were investigated in pure gas experiments. The results showed that CO2 and CH4 permeances decreased with increasing FA/PVA mass ratio, in comparison with uncross-linked membranes, although the selevtivities increased considerably. The highest selectivity (about 92.72) was achieved from PVA/FA(5wt%)/PTFE membrane. Moreover, it was found that CO2/CH4 selectivity was significantly decreased with increasing cross-linker/PVA mass ratio from 1 wt% to 5 wt%. On the other hand, the cross-linked membranes revealed favorable CO2/CH4 permselectivities in comparison with uncross-linked ones.